The liquid quenching method was adopted to study the solidification morphology and microstructure of AZ91D Mg alloy in semisolid. The results indicate that cooling rate has important effects upon the solidification structures. Under the cooling rate of liquid quenching, primary α-phase grows first by attaching on the original α grains, or independent nucleation and growth. The high cooling rate makes primary α-phase grow in "rags" or dendrite shape. Eutectic solidification is carried out in terms of both dissociated growth and symbiotic growth. The dissociated growth forms rough and large β-phase at grain boundaries, while symbiotic growth forms eutectic of laminar structure. The small liquid pool inside the original α-phase solidifies basically in the same way as that of intergranular liquid, but owing to less amount of liquid phase, the eutectic solidification is mainly carried out in the dissociated pattern.
关键词:
Magnesium alloy
,
液淬
,
凝固方式
,
凝固组织
Jinfeng XU
,
Qiuya ZHAI
,
Sen YUAN
材料科学技术（英）
Energy-storage welding connection characteristics of rapidly solidified AZ91D Mg alloy ribbons with 40~70 μm thickness are investigated using a microtype energy-storage welding machine. The microstructure and performance of the connection joints are analyzed and studied. The research results indicate that energy-storage welding is able to realize the spot welding connection of AZ9ID Mg alloy ribbons. The welding nugget consists of developed α-Mg equiaxed grains with the sizes of 1.2~2.7 μm and intergranular distributed β-Mg17Al12 compounds. The thickness of bond zone is about 4 μm and the solidification microstructure is characterized by the fine equiaxed grains with the sizes of 0.8~1.2 μm, and grain boundary has become coarsening. The columnar crystal in HAZ also becomes slightly coarsening and the grain boundary has broadened, however, there is no obvious change in its primitive morphology and crystallographic direction. When welding energy is about 2.0 J, the welding joints with higher shear strength and smaller electrical resistivity are obtained.
关键词:
AZ91D
,
null
,
null
,
null
,
null